Suit for brazing copper,steel,hard metal,etc,economical.
S226
890
905
Suit for brazing copper,steel,hard metal,etc,economical.
106
880
909
High strength of the joint suit for brazing hard metal instrument under heavy operating load below 500
Phos-copper-silver brazing rings
Product Number
Related Standard
Chemical Composition
Melting Range(°C)
Application
Ag
P
Cu
Solidus
Liquidus
GB-2B
BCu91PAg
1.8-2.2
6.8-7.2
Bal.
645
788
For brazing copper parts in airconditioners, freezers, refrigerators and motors. The brazing performance is excellent.
BCuP-6
1.8-2.2
6.8-7.2
Bal.
645
788
L-Ag2P
2.0
6.2
Bal.
645
825
GB-5B
BCu89PAg
4.8-5.2
5.8-6.7
Bal.
645
815
BCuP-3
4.8-5.2
5.8-6.2
Bal.
645
815
BCuP-7
4.8-5.2
6.5-7.0
Bal.
645
785
L-Ag5P
5.0
6.0
Bal.
645
815
GB-6B
BCu87PAg
5.8-6.2
7.0-7.5
Bal.
645
724
BCuP-4
5.8-6.2
7.0-7.5
Bal.
645
724
GB-15B
BCu80AgP
14.5-15.5
4.8-5.2
Bal.
645
800
BCuP-5
14.5-15.5
4.8-5.2
Bal.
645
800
L-Ag15P
15.0
5.0
Bal.
645
800
GB-18B
BCu75PAg
17.5-18.5
6.0-6.5
Bal.
645
680
For brazing copper and copper alloys in motors,transformation equipment and spectacles.
18M
18.0
6.3
Bal.
645
680
L-Ag18P
18.0
7.05
Bal.
645
645
Aluminium Brazing Rings
Aluminium Brazing Ring is a welding ring that container magnesium aluminum filler metal. The weld deposit of this filler metal offers good corrosion resistance when exposed to salt water. This alloy is commonly used on base metals 5050,5052,5083,5356,5454 and 5456. The post-anodizing color tint of the weld area is white.
TYPICAL MECHANICAL PROPERTIES
Tensile strength:269 MPa
Yield strength:132MPa
Elongation:17%
Melting Point:571-635°C
Processing Temp.:600-645°C
Thermal Conductivity:~100W/m°C
27.7%IACS
Electrical Resistivity:~6.0µΩcm
~28%IACS
Welding Process:MIG,TIG
Anodizing: Excellent
Corrosion Resistance: Excellent. Very good in marine atmosphere
Conductivity: Poor
Chemical Composition (%):
Cu1.8-2.2, Mg4.5-5.5,other<0.5, Al:bal.(There are different composition for different models of Aluminium Brazing Ring )
APPLICATION
Parent Metals:5000 series alloys(AlMg) with Mg<4%,6000(AlMgSi) alloys when anodized. Cast alloys of AlSi-Mg type. In practice the most versatile and universally used filler metal.
Silver Brazing Ring
————–Cd Free Silver Brazing Alloy
Brazing alloy
Standards
Compisition/%
Melting Range
/℃
Application
Ag
Cu
Zn
XR-Ag25
GB:BAg25CuZn
24.0-26.0
40.0-42.0
Bal.
700-800
An economical low silver filler metal used for ferrous metals, stainless steel, copper, brass except aluminum, used in mechanical and electrical industries, refrigeration, musical instruments.
XR-Ag45
GB:BAg45CuZn
AWS:BAg-5
44.0-46.0
29.0-31.0
Bal.
665-745
It is an excellent filler metal for brazing brass parts (such as ships piping, band instruments, aircraft engine oil coolers, brass lamps etc).
XR-Ag65
GB:BAg65CuZn
AWS:BAg-9
64.0-66-0
19.0-21.0
Bal.
685-720
Used particularly for joining sterling silver. Good color match with sterling silver.
—————Cd/In Containing Silver Brazing Alloys
Brazing alloy
Standards
Compisition/%
Melting Range/℃
Application
Ag
Cu
Zn
Cd
In
XR-Ag20Cd
GB:BAg20CuZnCd
19.0-21.0
39.0-41.0
Bal.
13.0-17.0
—
605-765
Have good fillet forming properties with ability to bridge wide gaps. Their wide melting range limits their applications. Due to their wide melting range they are somewhat more subject to liquation and may require more care during brazing. Therefore, they are not normally recommended for applications with slow heating rates.
XR-Ag25Cd
GB:BAg25CuZnCdAWS:BAg-33
24.0-26.0
29.0-31.0
Bal.
16.5-18.5
—
607-682
XR-Ag35Cd
GB:BAg35CuZnCdAWS:BAg-2
34.0-36.0
25.0-27.0
Bal.
17.0-19.0
—
605-700
A free flowing general purpose brazing alloy. It’s broader melting range is helpful where clearances are wide or are not uniform. Unless heating is rapid, care must be taken that the lower melting constituents do not separate out by liquation.
XR-Ag50Cd
GB: BAg50CuZnCdAWS: Bag-1a
49.0-51.0
14.5-16.5
Bal.
17.0-19.0
—
625-635
One of the lowest melting point silver brazing alloys available. It has excellent flow characteristics. The highest joint strength can be obtained with this alloy. Has better resistance to corrosion in chlorine, sulphur and steam environments.
XR-Ag18In
—
17.0-19.0
46.0-48.0
Bal.
—
0.8-1.2
792-810
An economical low silver filler metal used for ferrous metals, stainless steel, copper, brass except aluminum, used in mechanical and electrical industries, refrigeration.
XR-Ag34In
GB:BAg34CuZnIn
33.0-35.0
34.0-36.0
Bal.
—
0.8-1.2
660-740
It is an excellent filler metal for brazing compressor parts.